Aluminum plate manufacturers share with you: aluminum is one of the non-ferrous metals in the metal category. Due to its wide application, it is introduced separately as follows: there are two kinds of commonly used aluminum profiles and die-casting aluminum alloys. Among them, aluminum ingots with purity of more than 92% are used as the main raw materials, and metal elements such as carbon, magnesium, silicon and sulfur are added to increase strength, hardness and wear resistance to form a variety of "alloys".
1.1 aluminum profile
The surface quality of aluminum profile also has some defects that are difficult to overcome: warpage, deformation, black line, convex concave and white line. The designer with high level and reasonable die design and production process can avoid the above defects. The defects shall be inspected according to the inspection method specified by the state, that is, the sight distance is 40 ~ 50cm to judge the defects.
Aluminum profiles are widely used in furniture: screen framework, various suspension beams, table feet, decorative strips, handles, wiring ducts and covers, chair tubes, etc., which can be designed and used in thousands of ways!
Although aluminum profile has many advantages, it also has some disadvantages:
Aluminum without oxidation treatment is easy to "rust", resulting in performance degradation, and its longitudinal strength is not comparable to that of iron products The wear resistance of the surface oxide layer is not as good as that of the electrodeposited coating, and it is easy to scratch The cost is high, which is about 3 ~ 4 times higher than that of iron products.
1.2 die cast aluminum alloy
Compared with the processing methods of die-casting alloy and profile, the equipment used is different. Its raw materials are aluminum ingot (purity about 92%) and alloy materials, which are melted in the furnace and molded in the die-casting machine. The shape of die-casting aluminum products can be designed like toys, with different shapes, which is convenient for connection in various directions. In addition, it has high hardness and strength, and can be mixed with zinc into zinc aluminum alloy at the same time.
Die casting aluminum forming process is divided into:
1. Die casting
2. Rough polishing to remove the remaining mold material
3. Fine polishing
On the other hand, in the production process of die-casting aluminum, it can only be manufactured with molds. The cost of molds is very expensive, which is higher than that of injection molds and other molds. At the same time, mold maintenance is very difficult, and it is difficult to reduce materials and repair when the design is wrong.